Applications
Manufactured by co-extrusion polyolefin and polyamide, it has excellent tensile strength,
puncture resistance and waterproof properties. Specially designed for environment sealing
and protection of crimp splices and terminations.
Features
Shrink ratio: 3:1
Excellent puncture resistance
High peel strength.
Abrasion and corrosion resistance.
Waterproof and moisture resistance.
Various
Operating temperature: - 55°C to +125°C
Minimum shrink temperature: 80°C
Minimum fully recovery temperature: 130°C
Standard color: Red, blue, yellow

Technical Data

Property	Test Method	Values
Tensile strength	Room temp	≥16  MPa
Elongation at break		≥200%
Voltage withstand and breakdown Voltage		Withstand 2.5KV for 1minute and breakdown
Tensile strength at aging	158℃/7days	≥11.5 MPa
Elongation at break at aging		≥100%
Voltage withstand and breakdown Voltage at aging		At least half of un-aged breakdown voltage
Copper  corrosion		No sign of degradation
Copper stability		No drop, no flow
Cold  bend	-30℃/4 hrs	No  cracking
Maximum  secant  modulus   (2%)		250MPa
Volume resistivity		Min.1014 Ω·cm
Heat  shock	250°C/4 hrs	No  cracking

Dimensions

As Supplied (mm)		After Recovery (mm)		Standard length
Inside Diameter Min. (D)	Wall Thickness Min. (WT)	Inside Diameter Min. (D)	Wall Thickness Min. (WT)	m/roll
Φ3.2±0.3	0.35±0.05	Φ1.0	1.0±0.1	100
Φ4.8±0.3	0.45±0.05	Φ1.4	1.1±0.1	100
Φ7.0±0.3	0.45±0.05	Φ2.5	1.2±0.1	100
Φ6.8±0.3	0.5±0.05	Φ3.0	1.4±0.1	100
Φ7.0±0.3	0.5±0.05	Φ2.5	1.5±0.1	100
Φ8.3±0.3	0.65±0.05	Φ3.0	1.65±0.1	100