Applications
Suitable for resistance to aviation and diesel fuels, hydraulic
fluids, lubricating oils and chemical solvents. Ideal for the protection of cable,
wiring harnesses and connectors in military vehicles and motor sport.

Features
Cross-linked specially formulated elastomeric compounds.
Flexible, flame-retardant.
Excellent resistance to oil, diesel and hydraulic fluids.

Various
Operating temperature : -75°C to +150°C
Shrink temperature: 150°C
Shrink ratio: 2:1

Technical Data

Property		Test Method	Typical Data
Physical	Operating    temperature	UL224	-75°C to+150℃
	Longitudinal   shrinkage	ASTM D2671	≤0.5%
	Tensile  strength	ASTM D2671	>13 MPa
	Elongation  at  break	ASTM D2671	≥400%
	Tensile strength at aging 150°C/168hrs	ASTM D2671	≥12Mpa
	Elongation at break at aging 150°C/168hrs	ASTM D2671	≥300%
	Heat  shock   (215°C/4hrs)	ASTM D2671	No cracking
	Low Temperature flexibility (-75°C/4hrs)	ASTM D2671	No cracking
Electrical	Dielectric voltage withstand	ASTM D2671	2500V,60s No breakdown
	Volume    resistance	ASTM D2671	≥1010Ω.cm
	Dielectric strength	ASTM D2671	≥16/KV/mm
Chemical	Flammability	ASTM D2671	Self-extinguish in 60s
	Copper    corrosion	ASTM D2671	No corrosion
Fluids resistance  (23°C/24hrs)	Tensile  strength	ASTM D2671	>12MPa
	Elongation  at  break	ASTM D2671	≥300%
	Dielectric  strength	ASTM D2671	≥12KV/mm

Dimensions/Shrink ratio 2:1

Size As Supplied (mm)	Size After Recovery(mm)		Standard length m/spool
Inside Diameter Min. (D)	Inside Diameter Max. (d)	WT. (mm)
2.4	1.2	0.76±0.15	200
3.2	1.6	0.76±0.15	200
4.8	2.4	0.84±0.15	100
6.4	3.2	0.89±0.15	100
9.5	4.8	1.02±0.2	50
12.7	6.4	1.22±0.2	50
19.1	9.5	1.45±0.28	50
25.4	12.7	1.78±0.28	25
38.1	19.1	2.41±0.41	25
50.8	25.4	2.79±0.41	25